Effect of Titanium Hardness on the Integrity and Stress Concentration of External Hexagon Dental Implants

ABSTRACT: The aim of this study was to evaluate the influence of overtorque on integrity, strength and stress on external hexagonal implants (EH), with two different grades (N=10): conventional (C), grade 4; and modified (M), grade 4 with thermal treatment. The dimensions of EH were 3.75 x 13 mm; the specimens were fixed and submitted to SEM analysis and image acquisition. The abutment was then retained with 70 N/cm, re-analyzed by SEM, and a second image was obtained. The images were analyzed by Image J software (1.44o- NIH, USA) for dimensional variations measurement on surface of the hexagonal area. The finite element method was applied with a similar compliance to calculate the resultant stress (MPa) during the torque. Results were statistically analyzed with t-student test (5 %). The dimensional accuracy of M (0.22 mm2) was statistically significant (p<0.05). Minimum principal stress and von-Mises stress of C (-19.95 MPa, -19.94 MPa), were lower than M values (-55.83 MPa, -55.96 MPa), respectively. However, the M group showed lower deformation than C group. Therefore, more rigid titanium alloy is a promising alternative to avoid plastic deformation of prosthetic connec tions even concentrating higher stress magnitude on its structure.

RESUMEN: El objetivo de este estudio fue evaluar la influencia del sobrepar en la integridad, la fuerza y la tensión en los implantes hexagonales externos (EH), con dos grados diferentes (N = 10): convencional (C), grado 4; y modificado (M), grado 4 con tratamiento térmico. Las dimensiones de EH eran 3,75 de diámetro x 13 mm de longitud; las muestras se fijaron y se sometieron a análisis SEM y adquisición de imágenes. A continuación, el pilar se retuvo con 70 N / cm, se volvió a analizar por SEM y se obtuvo una segunda imagen. Las imágenes se analizaron con el software Image J (1.44o-NIH, EE. UU.) Para medir las variaciones dimensionales en la superficie superior del área hexagonal, que fue causada por un par excesivo. El método de los elementos finitos se aplicó con un cumplimiento similar para calcular la tensión resultante (MPa) durante el par. Los resultados se analizaron estadísticamente con la prueba t-student (5 %). La precisión dimensional de M (0,22 mm2) fue estadísticamente significativa (p <0,05). La tensión principal mínima y la tensión de von-Mises de C (-19,95 MPa, -19,94 MPa), fueron inferiores a los valores de M (-55,83 MPa, -55,96 MPa), respectivamente. Sin embargo, el hexágono del grupo M mostró menor deformación que el grupo C. Por lo tanto, la aleación de titanio más rígida es una alternativa prometedora para evitar la deformación plástica de las conexiones protésicas incluso concentrando una mayor magnitud de tensión en su estructura.

Edentulism in Brazil: trends, projections and expectations until 2040 / Edentulismo no Brasil: tendências, projeções e expectativas até 2040

Abstract The aim of this study was to examine the edentulism rates in Brazil and make projections for the next years. Data were collected from three national oral health surveys. The percentage of edentulous jaws was calculated. Projections were made for the years 2020, 2030 and 2040, assuming that edentulism follows a logistic function. Population projections were also performed. Annual change in proportion of edentulous jaws was -0.04% for teenagers, -0.96% for adults and 0.76% for the elderly. By 2040, edentulous jaws will be virtually zero among teenagers, 1.77% among adults and 85.96% among the elderly. Teenagers will slightly decrease in number; adults will increase and subsequently decrease; the elderly will continue to increase. In teenagers and adults, the number of edentulous jaws will decrease, being approximately 616,000 in 2040. In the elderly, it will increase alarmingly, reaching over 64 million in 2040. Edentulism is declining in Brazil among teenagers and middle-aged adults, but is still increasing and will continue to increase for the next decades among the elderly.

Resumo O objetivo deste estudo foi examinar as taxas de edentulismo no Brasil e fazer projeções para os próximos anos. Os dados foram coletados de três censos nacionais de saúde bucal. O percentual de arcadas edêntulas foi calculado. Foram feitas projeções para 2020, 2030 e 2040, assumindo que o edentulismo segue uma função logística. Também foram realizadas projeções populacionais. A variação anual da proporção de arcadas edêntulas foi de -0,04% para jovens, -0,96% para adultos e 0,76% para idosos. Até 2040, o percentual de arcadas edêntulas será virtualmente zero entre jovens, 1,77% entre adultos e 85,96% entre idosos. O número de jovens vai diminuir levemente; o de adultos vai aumentar e depois diminuir; e o de idosos vai continuar aumentando. Para jovens e adultos, o número de arcadas edêntulas vai diminuir, aproximando-se de 616.000 em 2040. Para os idosos, este número vai aumentar alarmantemente, alcançando mais de 64 milhões em 2040. O edentulismo está diminuindo no Brasil entre jovens e adultos, mas está aumentando e continuará a aumentar nas próximas décadas entre os idosos.

Levantamento de assoalho de seio maxilar û técnicas e materiais para enxertia / Sinus lift û grafting techniques and materials

Repor dentes perdidos através de implantes dentários é cotidiano nas clínicas odontológicas. O posicionamento desses implantes em posição ideal nem sempre é possível, devido às perdas ósseas e às limitações anatômicas que o paciente pode apresentar. Na maxila superior posterior a presença do seio maxilar pode ser um fator complicador para fixação dos implantes, além de que com a pneumatização do mesmo, pode evoluir a um osso muito delgado com uma fina camada cortical. Reabilitar esse tipo de paciente através de implantes pode ser impossível sem a utilização de materiais e técnicas capazes de repor parcial ou total a deficiência óssea, e suportar, em função, os implantes dentários. Atualmente, existem diversos materiais que podem ser utilizados isolados ou em conjunto com outros para levantamento do assoalho do seio maxilar, podendo deixar o cirurgião dentista em dúvida de qual material escolher para cada caso. Esta revisão tem como objetivo transcorrer sobre os materiais de enxertia disponíveis no mercado, baseado em evidências científicas, a fim de esclarecer para o cirurgião quais os substitutos ósseos disponíveis para utilização desse tipo de enxertia...

The treatment with dental implants after teeth loss has become a common practice in dentistry. However, the appropriate implant positioning can be compromised by bone resorption and anatomical limitations presented by mandible/maxilla. The presence of maxillary sinus on posterior region of an edentulous maxilla can hinder maxillary implants, mainly when sinus pneumatization occurs, leading to an insufficient volume of healthy bone for implantÆs placement. Oral rehabilitation with dental implants in such cases may not be executed without previous reconstructive surgical techniques associated to materials that will be able to create adequate bone volume for implant sites. Several materials are available and can be used alone or combined for maxillary sinus floor elevation. Thus their indications should be clarified aiming to guide dental surgeons. This literature review aims to discourse about marketed grafting materials, based on scientific evidence, clarifying which materials are the available for bone replacement on sinus lift...

Microdeformation of Infrastructure for Implant-Supported fixed Dental Prosthesis by Strain-Gauge Method: Influence of Technique and Material Impression

To verify the structural microdeformationby strain gages, around implants that have metal infrastructure, obtained by different materials and techniques impressions.Material and Methods:Three internal hexagon implants in polyurethane block (master model) with abutments were taken the impression with differents materials and techniques impression (n=4): addition silicon and transfer for open tray technique (Group I), condensation silicon and transfer for closed tray technique (Group II); and polyether and transfer for open tray techniques (GroupIII). Impressions were poured with type IV stone. Metallic infrastructure were made and installed in the master model by an aid of a manual ratchet wrench. A torque of 20N was used to install the metallic infrastructure. Microdeformation analysis was performed around the implants by strain gauge method. Two gauges were inserted into the polyurethane base, and three measurements were taken for each infrastructure. Data were analyzed using descriptive statistics and inference. Kruskal-Wallis test was used toverify association between materials and impression techniques and deformation around the implants, at 5% confidence.Results:Microdeformationsaround the implants showed no statistically significant difference (p = 0.123) between the experimental groups, Group I (215.8 με), Group II (194.9 με) and Group III (297.4 με). Conclusion:The use of different materials and techniques impression to madeof infrastructures for fixed implant-supported dental prosthesis did not present difference in microdeformation values around implants...

Métodos de caracterização de materiais para pesquisa em odontologia / Materials characterization methods in dentistry research

Esta revisão tem por finalidade esclarecer alguns pontos relevantes a respeito de algumas técnicas utilizadas em odontologia para caracterização dos materiais. Após um levantamento bibliográfico de 2006/2011 na base de dados PubMed, a microscopia eletrônica de varredura e a espectroscopia no infravermelho por transfor mada de Fourier foram as técnicas mais utilizadas para cada método de caracterização (microscopia e espectroscopia). Porém, outras técnicas têm sido utilizadas na caracterização dos materiais na pesquisa em odontologia.

Efeito da desinfecção associada à escovação na rugosidade superficial de resina acrílica termopolimerizável / Effect of disinfection associated to brushing on surface roughness of heat-polymerized acrylic resin

O objetivo desse estudo é avaliar o efeito da desinfecção associada à escovação na rugosidade (Ra e Rz) superficial de resina acrílica termopolimerizável. Cinquenta cilindros de resina acrílica (Lucitone 550 Dentsply) de dimensões 0,5 mm x 0,5 mm foram confeccionados, utilizando-se o ciclo térmico curto de polimerização (73°C por 90 min, seguidos por imersão em água a 94°C durante 30 min), de acordo com as instruções do fabricante. Os espécimes termopolimerizados foram imersos em água destilada a 37 ±1°C por 48 horas e divididos em 5 grupos (n=10) de acordo com o método de desinfecção: GrControle- sem desinfecção e sem escovação; Gr1-água destilada seguido de escovação; Gr2- hipoclorito de Sódio 1% seguido de escovação; Gr3- gluconato de clorexidina 2% seguido de escovação, e G4- perborato de sódio a 3,78% seguido de escovação. Os grupos foram imersos por 5 min nas soluções correspondentes antes do ciclo de escovação (10.000 ciclos). Foram analisados em rugosímetro de contato os valores para Ra e Rz. Os resultados foram analisados estatisticamente pelo método ANOVA e as médias comparadas pelo teste de Tukey (α=0,05). As médias obtidas para o Ra e Rz respectivamente foram: Gr controle 0,16 (0,03) e 0,77 (0,21); Gr1 0,3 (0,13) e 1,25 (0,62); Gr2 0,24(0,09) e 1,02 (0,4); Gr3 0,34 (0,14) e 1,45(0,55); Gr4 0,38(0,14) e 1,7(0,65). O teste ANOVA revelou que a rugosidade para os dois parâmetros foi significativamente afetada pela abrasão provocada pela escovação com dentifrício (PRa=0,0009; PRz=0,0021). Pode-se concluir que a escovação associada à desinfecção com hipoclorito de sódio produziu menor efeito sobre a rugosidade da superfície da resina acrílica que os demais desinfetantes testados.

The aim of this study was to evaluate the effect of disinfection associated to brushing the superficial crease (Ra and Rz) of heat-polymerized acrylic resin. Fifty cylinders of 0.5mm x o.5mm acrylic resin (Lucitone 550 Dentsply) were produced by using the short thermal cycle of polymerization (73ºC for 90 minutes and then immersion on water at the temperature of 94ºC for 30 minutes), according to the manufacturer’s instructions. The thermo-polymerized samples were immersed in distilled water at the temperature of 37ºC (plus or minus 1ºC) for 48 hours and divided into 5 groups (n=10) according to the disinfection method, that is: GrControl – no chemical disinfection nor brushing; Gr1 – distilled water and brushing; Gr2 – sodium hypoclorite 1% and brushing; Gr3 – chlorexidine gluconate 2% and brushing and G4 – sodium perborate 3,78% and brushing. The groups were immersed for 5 minutes before brushing cycle (10.000 cycles) and the values for Ra and Rz were analyzed with crease contact measuring instrument(contact profilometer). Results were statistically analyzed by the ANOVA method. The arithmetic means were compared by the Tukey test (ά=0.05). RESULTS: The arithmetic means obtained for Ra and Rz were : GrControl 0.16(0.03) and 0.77 (0.21); Gr1 0.3(0.13) and 1.25(0.62); Gr2 0.24(0.09) and 1.02(0.4); Gr3 0.34(0.14) and 1.45(0.55); Gr4 0.38(0.14) and 1.7(0.65) . The ANOVA test revealed that the roughness for the two parameters was significantly affected by brushing with toothpaste (PRa =0.0009; PRz=0.0021) .Tooth brushing together with sodium hypoclorite results in a lessened effect over the surface crease of the acrylic resin than other tested disinfectants

Avaliação in vitro da resistência à compressão de condicionadores de tecido submetidos a diferentes tempos de armazenamento / In vitro evaluation of the compressive strength of tissue conditioners submitted to different storage times

Objetivou-se avaliar in vitro a resiliência de dois condicionadores de tecido, UG - Ufigel SC (Voco) e D - Dentusoft (DMG), depois de serem submetidos a diferentes tempos de armazenamento em água destilada a 37ºC (24 horas, 14 dias, 30 dias e 180 dias). Foram confeccionadas 20 cápsulas de resina acrílica termicamente ativada, com 20 mm de diâmetro interno e 3 mm de profundidade. Os condicionadores de tecido, UG e D, foram manipulados de acordo com o fabricante, acomodados no interior das cápsulas (n = 10) e armazenados por 24 horas, 14 dias, 30 dias e 180 dias. Cada grupo foi submetido ao teste de resiliência utilizando uma ponta romba de 3 mm de diâmetro em máquina de ensaio universal (EMIC-DL 1000). Os dados foram submetidos à análise estatística two-way ANOVA e ao teste de Tukey (α = 0,05). Os valores de média para os materiais/tempo de armazenagem foram: UG/24 horas - 3,81A; D/30 dias - 5,54B; UG/14 dias - 5,58B; UG/30 dias - 5,66BC; UG/180 dias - 5,77BC; D/24 horas - 5,79BC; D/180 dias - 6,13C; D/14 dias - 6,54D. Dentusoft armazenado por 14 dias obteve valores de média de resiliência significantemente superiores em relação aos demais. Ufigel armazenado nos períodos de 1 a 14 dias apresentaram valores de resiliência menores do que D, sendo estatisticamente significante nesses períodos. Entretanto, para os períodos de avaliação de 30 e 180 dias, não se observaram diferenças significantes entre os materiais.

Próteses fixas em pacientes com suporte periodontal reduzido / Fixed partial dentures in patients with reduced periodontal tissue support

Alguns aspectos são controversos na reabilitação oral com próteses fixas em pacientes que apresentam extensas perdas das estruturas de suporte periodontal. O objetivo deste trabalho é esclarecer, por meio de uma revisão da literatura, estes pontos; bem como enfatizar as indicações e as características biomecánicas a serem observadas nesta modalidade de tratamento.

Efeito do uso de retificadores e do método de fundição em coroas unitárias implantossuportadas: análise em microscopia óptica e extensometria / Effect of rectifiers and casting methods in single-tooth implant-supported crowns: light microscopy and strain gauge analysis

Objetivo: avaliar, in vitro, a adaptação marginal de cilindros pré-fabricados de Co-Cr e cilindros plásticos fundidos em Ni-Cr a pilares do tipo Micro-Unit por meio da microscopia ótica, variando o método de fundição e o uso ou não de retificadores. Durante o ensaio verificou-se, por meio da extensometria, a tensão gerada ao redor do implante durante o aperto do parafuso. Material e Métodos: 36 cilindros tipo Micro-Unit foram subdivididos em três grupos (n = 12): G1 - pré-fabricados em Co-Cr (controle); G2 - fundidos em níquel-cromo (Ni-Cr) pelo método convencional; G3 - fundidos em Ni-Cr pelo método de indução. Para cada cilindro foram realizadas 32 leituras no microscópio óptico (200 x) e mensuração da tensão (extensometria) durante o aperto do parafuso de fixação, com torquímetro eletrônico. Posteriormente, os cilindros dos grupos 2 e 3 foram retificados formando dois subgrupos: G2b e G3b, os quais foram novamente analisados em microscópio óptico e na extensometria. Resultados: os valores (μm) para desadaptação marginal (média/desvio-padrão) nos grupos foram: G1- 33,3; G2a- 61,86 (16,6); G2b- 26,12 (5,5); G3a- 61,57 (22,7); G3b- 28,74 (6,9). Na extensometria (μƐ) foram: G1- 162,14; G2a- 185,42 (94,8); G2b- 168,75 (122,2); G3a- 105,42 (38,5); G3b- 92,0 (33,6). Conclusão: a retificação dos cilindros fundidos em liga de Ni-Cr reduziu significativamente a desadaptação marginal para ambos os métodos de fundição e o uso da técnica de fundição por indução diminuiu a microdeformação ao redor do implante.

Objective: to evaluate, in vitro by light microscopy, the marginal fit between microunit-like abutments and different types of cylinders. Also, strain gauge analysis was used to verify tension during screw tightening. Materials and methods: Thirty-six Microunit-like cylinders were subdivided into three groups: G1 (control) - 12 prefabricated cylinders (Co-Cr); G2 - 12 plastic cylinders (conventional casting in Ni-Cr); G3 - 12 plastic cylinders (casting for induction in Ni-Cr). Light microscopic analysis provided 32 measurements around the interface. The strains gauge analysis was carried with a 10Ncm torque under electronic torque-controlling device. After, the cylinders of G2 and G3 had been rectified forming two sub-groups: G2b and G3b, which again had been analyzed according to the same methods. Results: Mean and SD values of marginal fit (μm) were: G1- 33.3; G2a- 61.86 (16.6); G2b- 26.12 (5.5); G3a- 61.57 (22.7); G3b- 28.74 (6.9). Mean μƐ (SD) values were: G1- 162.14; G2a- 185.42 (94.8); G2b- 168.75 (122.2); G3a- 105.42 (38.5); G3b- 92.0 (33.6). Conclusion: the use of rectifiers in the Ni-Cr cast cylinders reduced the marginal fit for both casting methods and the use of the induction casting procedures diminished the μƐ values around implant.

Discrepâncias de assentamento ocorridas em copings cerâmicos confeccionados pelos sistemas IPS Empress 2 e In-Ceram, variando-se ostérminos cervicais e os agentes cimentantes: estudo in vitro / Adjustment discrepancies in ceramic copings made in IPS Empress and In-Ceram systems, varying the cervical end and the cements used: an in vitro study

Este trabalho avaliou as adaptações cervicais de copings cerâmicos, confeccionados pelos Sistemas Empress 2 e In-Ceram, variando-se os términos cervicais dos preparos em chanfro largo e ombro 90° arredondado; em preparos com 15° de conicidade, e 2 tipos de agentes para cimentação: o cimento de fosfato de zinco e um cimento resinoso. Foram confeccionados dois modelos-padrão de aço inoxidável. A partir destes obtiveram-se 40 troquéis em gesso tipo V, sendo 20 para cada sistema e 10 para cada tipo de término cervical e os copings cerâmicos correspondentes para cada sistema. Em seguida, o conjunto foi levado ao metroscópio horizontal para a primeira leitura (L0). Procedeu-se a cimentação, inicialmente sob pressão digital, em seguida com a aplicação de carga padronizada e efetuou-se a segunda medida (L1).Após a coleta dos dados, foi realizada a análise estatística das médias das medidas aferidas e as seguintes conclusões foram alcançadas: a) o cimento de fosfato apresentou um valor médio de discrepância de assentamento, para os dois sistemas, menor do que o resinoso; b) término cervical em chanfro e ombro arredondado, para qualquer um dos sistemas, mostraram resultados semelhantes; c) o sistema In-Ceram apresentou um valor médio de discrepância assentamento menor que o IPS Empress 2, porém não significante estatisticamente.

The aim of this study was to assess the cervical adjustments of ceramic copings, using two ceramic systems, the Empress 2 and In-Ceram, varying the cervical end of the preparations and the types of cements: zinc phosphate and resin cement. Initially two standard models of stainless steel were made. From these models 40 stone dies were made, 20 for each system and 10 for each type of cervical end. A specialized commercial laboratory made the ceramic copings corresponding to each system. Then, the set was brought to the horizontal metroscopic for first measure, called L0. The cementing process was done, initially under digital pressure, and then with the implementation of standardized load, when the second measure, called L1, was done. After collecting the data, statistical analysis was carried out. We could conclude that- a) zinc phosphate cement showed less settlement discrepancy, for both systems, than the resin cement b) rounded shoulder and chamfer ends showed similar results, c) In-Ceram system had less settlement discrepancy, but not statistically significant, than IPS Empress 2.

Influência de diferentes dispositivos de microtração nos valores de resistência coesiva / Influence of different devices on microtensile strength

O objetivo deste estudo foi avaliar a influência de dispositivos de microtração sobre a resistência coesiva de blocos de resina acrílica. Vinte blocos de resina acrílica termopolimerizável (Onda-Cryl Clássico) foram confeccionados e distribuídos em 4 diferentes grupos experimentais (n=5) de acordo com o dispositivo de microtração empregado: G1: Paquímetro modificado; G2: Dispositivo de Andreatta Filho; G3: Dispositivo de Borges; G4: MT-jig. Os blocos foram seccionados em palitos de lmm2 e submetidos ao teste de microtração (EMIC DL 1000). Os dados foram avaliados pela Análise de Variância e pelo Teste de Tukey, a 5% de significância. Os menores valores de resistência mecânica foram obtidos com os dispositivos de Andreatta Filho (34,22 MPa) e de Borges (34,49 MPa), e os maiores valores com o Paquímetro modificado (49,44 MPa) e o MT-jig (48,40 MPa). Concluiu-se que os valores de resistência mecânica são influenciados pelos dispositivos de microtração utilizados e que não podem ser comparados entre si.

The aim of this study was to assess the influence of different devices on microlensile strength of acrylic resin blocks. Twenty thermo polyrnerized acrylic resin blocks (Onda-Cryl Clássico) were produced and divided into four experimental groups (n=5) according to microtensile device used: G I: Modified caliper; G2: Andreatta Filho’s device: G3: Borges' device: G4: MT-jig. Blocks were sectioned into sticks with a crosssection of I rnm2- and tested to failure in tension mode (EMIC DL 1000). The data were submitted to l-way analysis of variance (AOVA), followed by Tukey’s test (a=.05). The lowest mean microtensile strengths were obtained with Andreatta Filhos (34.22 MPa) and Borges' (34.49 MPa) devices. Paquimeter (49.44 MPa) and MT-jig (48.40 MPa) promoted the highest mean microtensile strengths, 1t was concluded that microtensile devices influence mechanical strength values.

Avaliação da variação da temperatura intrapulpar após o uso de agentes clareadores e ativação por fontes de luz / Evaluation of the variation of intrapulpal temperature after the use of bleaching agents and activation by light sources

Introdução e objetivo: Buscou-se avaliar in vitro o grau de aquecimento promovido no interior da câmara pulpar após o uso de diferentes agentes clareadores, com ou sem ativação por fontes de luz. Material e métodos: Foram utilizados 60 dentes incisivos bovinos, que receberam acesso ao canal radicular pela face lingual, com a parede vestibular padronizada em 2 mm. Os espécimes foram divididos em 6 grupos (n = 10), de acordo com o agente clareador e a fonte de ativação utilizada: G1 - ausência de agente clareador e aplicação de luz halógena; G2 - ausência de agente clareador e aplicação de LED; G3 - aplicação do agente clareador Whiteness HP Maxx (peróxido de hidrogênio 35%) e ativação com luz halógena; G4 - aplicação do agente clareador Whiteness HP Maxx (peróxido de hidrogênio 35%) e ativação com LED; G5 - aplicação do agente clareador Opalescence Xtra Boost (peróxido de hidrogênio 38%) e ativação com fotopolimerizador; G6 - aplicação do agente clareador Opalescence Xtra Boost (peróxido de hidrogênio 38%) e ativação com LED. A variação da temperatura na câmara pulpar foi mensurada com um aparelho termopar. Resultados: Os valores de temperatura foram medidos pelo aparelho durante 10 minutos, com alguns intervalos selecionados: t1 - temperatura inicial; t2 - após 25 segundos de aplicação do gel e 20 segundos de ativação; t3 - após 10 minutos. Os valores obtidos foram registrados pela máquina no software, e os dados foram submetidos à análise estatística pelo teste Anova. Verificou-se que o aumento da temperatura não foi significante em todos os grupos testados. Conclusão: Não foram encontradas diferenças estatisticamente significantes entre os grupos com e sem ativação por fontes de luz ou entre os diferentes clareadores.

Introduction and objective: To evaluate in vitro the degree of warming promoted within the pulp chamber, after the use of bleaching agents, with or without activation by light sources. Material and methods: Sixty bovine teeth were used, which had received access to the root canal by the side lingual, with the wall vestibular standardized at 2 mm. The specimens were divided into 6 groups (n = 10), according to the bleaching agent and the source of activation used: G1 - absence of bleaching agent and application of halogen light; G2 - absence of bleaching agent and application of LED; G3 - application of the Whiteness HP Maxx (35% hydrogen peroxide) and activation with halogen light; G4 - application of Whiteness HP Maxx (35% hydrogen peroxide) and activation with LED; G5 - application of the Opalescence Xtra Boost (38% hydrogen peroxide) and activation with photopolymerizer; G6 - application of the Opalescence Xtra Boost (38% hydrogen peroxide) and activation with LED. The change of temperature in the pulp chamber was measured using a Termopar apparatus. Results: The values of temperature were measured by the device during an interval of 10 minutes, with some selected intervals: t1 - initial temperature; t2 - after 25 seconds of application of the gel and 20 seconds of activation; t3 - after 10 minutes. The values were registered by the machine in the software and the data were subjected to statistical analysis using the Anova test. Conclusion: There were no statistically significant differences between groups with and without activation or between different bleaching.

Avaliação in vitro de três condicionadores de tecido, submetidos a testes de penetração / In vitro evaluation of three temporary tissue conditioners, submitted to penetration tests

Introdução e Objetivo: O objetivo do estudo foi avaliar a existência de alterações na resiliência de quatro diferentes condicionadores de tecido: Coe Comfort (CC), Ufi-Gel (UG), Sofreliner S (SS) e Sofreliner MS (SMS), associados aos seus respectivos selantes de superfície em diferentes intervalos de tempo. Material e Método: Foram confeccionadas 160 cápsulas de resina acrílica que, após seu acabamento, foram preenchidas com os condicionadores de tecidos. Para o Grupo CC, não houve tratamento da superfície interna das cápsulas, sendo o material preparado conforme as indicações do fabricante e acomodado nas cápsulas e para os condicionadores de tecido UG, SS e SMS realizou-se o tratamento interno das cápsulas. Após a obtenção dos corpos de prova, estes foram submetidos a testes de penetração, os testes foram realizados nos intervalos de 1h, 24hs, 30, 60 dias. Resultados: Avaliou-se o efeito do fator tempo na resiliência destes materiais e foi observado que o CC foi o condicionador que mais perdeu essa característica com o passar do tempo, comprovando que seu uso está limitado apenas por curto período. Já os condicionadores UG, SS e SMS, apesar de terem uma pequena deficiência na resiliência na primeira hora, demonstraram-se mais estáveis após todos os testes ao final de 60 dias. Conclusão: Condicionadores de tecidos a base de silicona permanecem com as características iniciais por até 60 dias, enquanto condicionadores de tecido a base de resina acrílica perdem progressivamente sua viscoelasticidade.

Introduction and Objective: The aim of this study was to evaluate resilience changes of four tissue conditioners: Coe Comfort (CC), Ufi-Gel (UG), Sofreliner S (SS) and Sofreliner MS (SMS), associated to their respective surface sealers at different times. Material and Method: 160 capsules of acrylic resin were made and then finished prior to the filling with the tissue conditioners. For the CC group the capsules were not treated and were filled with the material. For the conditioners UG, SS and SMS, the capsules were internally treated prior to the material insertion. All the materials were used following the manufacturer?s instructions. The test were carried out after 1h, 24h, 30 days and 60 days. Results: The effect of time at the materials resilience was evaluated and observed that CC loses more resilience than UG, SS and SMS what proofs his use in a short period. UG, SS and SMS despite bad results in a first moment, shows better results after 60 days. Conclusion: Were concluded that silicon based materials are more stable than acrylic resin based materials.

Altura de los tallados coronales en la retención de prótesis parcial fija / Height of crown carved on the retention of fixed partial denture

La altura y convergencia de las paredes axiales, el diámetro de los tallados, la presencia de surcos para mejorar la retención y el tipo de cemento son algunas de las condiciones que influencian el ajuste y la retención de las restauraciones fundidas. El objetivo de este trabajo fue verificar larelación de la cantidad de retención con el aumento gradual de la altura de los tallados coronales. Usando 11 troqueles y 11 cápsulas metálicas, fresados y perfectamente adaptados, con alturas desde 3mm hasta 8mm, con el aumento gradual de 0,5mm. Todas las capsuladas fueron cementadas de forma estandarizada y luego de 24 horas fueron sometidas a la prueba de tracción (EMIC - 1000). Los resultados mostraron que incrementos de 0,5mm en la altura del tallado aumentaron en promedio de 7N la resistencia a tracción de los cuerpos de prueba, por tal motivo se puede concluir que existe una influencia de la altura del tallado en la capacidad retentiva de los troqueles.

The height and convergence of axial walls, the diameter of the coronal preparation, the presence of grooves to improve retention and the type of cement are some of the conditionsthat influence the adjustment and retention of cast restorations. The aim of this study was to verify the relationship between the amount of retention with the gradual increase in the heightof the coronal preparation. Using 11 die and 11 metal capsules milled and perfectly adapted, with heights from 3mm to 8mm, with the gradual increase of 0.5 mm. All capsules were cementsin a standardized way, and after 24 hours were tested for tensile strength (EMIC-1000). The results showed increases of 0.5 mm in height of coronal preparations, rose 7N on average thetraction resistance of all tested bodies, therefore we can conclude that there is an influence of the height of the coronal preparation on the retention capacity of dies.

Pulpal temperature increase with high-speed handpiece, Er-YAG laser and ultrasound tips

The aim of this study was to compare intrapulpal temperature increase produced by high-speed handpiece, Er:YAG laser and CVDentus ultrasound tips during cavity preparation. Thirty bovine mandibular incisors with an enamel/dentin thickness of 4 mm at buccal surface had their roots amputated and were allocated to the following groups (n=10): Group I- high-speed handpiece; Group II- noncontact Er:YAG laser (250 mJ/4Hz); and Group III- CVDentus ultrasouns tips. All devices were used with water cooling. Class V cavities were prepared to a depth of 3.5 mm, measured with a periodontal probe. A type T thermocouple was placed inside the pulp chamber to determine the temperature increase (°C), which was recorded by a data acquisition system ADS 2000 IP (Lynx Technology) linked to a notebook computer. Data were analyzed statistically by oneway ANOVA and Tukey’s test (p=0.05). The mean temperature rises were: 1.10°C (±0.56) for Group I, 0.84°C (±0.55) for Group II, and 3.00°C (± 1.34) for Group III. There were no statistically significant differences (p>0.05) between Groups I and II, but both of them differed significantly from Group III (p<0.05). In conclusion, the use of Er:YAG laser and high-speed handpiece for cavity preparation resulted in similar temperature increase. Although ultrasound tips generated significantly higher intrapulpal temperature increase, it remained below the critical value of 5.5°C and may be considered safe for use.

Aderência de Candida albicans em ligas de titânio e cobalto-cromo, com diferentes desgastes / Adherence of Candida albicans in cobaltochromium and titanium alloys, with different sandpapering

Introdução: A capacidade de aderência de Candida albicans é um dos seus principais fatores de virulência. Superfícies de materiais diferentes podem propiciar condições para maior ou menor aderência e maior virulência dos microrganismos. Objetivo: Avaliar a aderência de Candida albicans em ligas de titânio e cobalto-cromo, com diferentes desgastes. Material e métodos: Foram confeccionados 24 corpos-deprova (CPs) cilíndricos, 12 de titânio e 12 de cobalto-cromo, divididos em 4 grupos de seis. Todos foram polidos de forma habitual pelo mesmo técnico. Os CPs foram lixados em torno de alta rotação por 15 segundos cada lixa, por toda a sua superfície. Um grupo de cada metal foi lixado apenas com lixa para metal número 80. Os dois outros grupos foram lixados conforme a seqüência (granulação decrescente): 80, 150 e 220. Os CPs foram esterilizados e posicionados em placas de cultura de células. Em cada poço da placa foi adicionada quantidade padronizada de caldo Sabouraud e suspensão contendo 106 céls./mL de C. albicans (ATCC 18804). Após incubação, o número de células aderidas por mm2 foi obtido pelo método de semeadura em placa de Petri. Os valores encontrados foram tabulados e submetidos aos testes de ANOVA e Tukey, com nível de significância de 5%. Resultados: Houve diferença estatística para a granulação de lixas, e não houve diferença quando foram comparados os metais. Conclusão: Quanto maior ?? a granulação final da lixa maior é a aderência, e o tipo de metal não influenciou no resultado.

Introduction: The capacity of Candida albicans adherence is one of its main factors of virulence. Surfaces of different materials can propitiate conditions for higher or lower adherence and greater virulence of the microorganisms. Objective: Evaluate the adherence of Candida albicans in cobalto-chromium and titanium alloys, with different sandpapering. Material and methods: Twenty-four cylindrical samples have been constructed, 12 of titanium and 12 of cobalt-chromium, divided in 4 groups of six. All have been polished in the habitual form by the same technician. Samples have been sandpapered at about high rotation for 15 seconds each sandpaper, on all its surface. A group of each metal was sandpapered only with sandpaper for metal number 80. The two other groups have been sandpapered in agreement with the sequence (decreasing granulation): 80, 150 and 220. Samples have been sterilized and located in plates of cells culture. In each well of the plate was added standardized amount of Sabouraud broth and suspension containing 106 cells per milliliter of C. albicans (ATCC 18804). After incubation, the number of adhered cells per mm2 was obtained by the method of sowing in plate of Petri. The obtained values have been tabulated and submitted to the tests of ANOVA and Tukey, with level of significance of 5%. Results: There was statistical difference for the granulation of sandpapers, what not occurred when considering metals. Conclusion: The bigger the final granulation of sandpaper, the greater the adherence and the type of metal did not influence in the result.

Avaliação clínica da adaptação de apoios em cíngulo para prótese parcial removível / A clinical study of the fit of cast cingulum rests for removable partial denture

O objetivo deste trabalho in vivo foi avaliar a adaptação de apoios em cíngulo confeccionados sobre esmalte ou resina composta em Próteses Parciais Removíveis. Após a prova e ajuste da armação metálica e anteriormente ao registro da relação maxilo-mandibular foram selecionados caninos com apoios considerados adaptados clinicamente, totalizando uma amostra de 16 apoios em esmalte (Grupo A) e 16 apoios em resina composta (Grupo B). A adaptação foi verificada utilizando uma silicona por condensação leve (Heraeus Kulzer). O material foi manipulado e colocado na face interna do apoio, em seguida a armação metálica foi inserida na boca de acordo com a trajetória de inserção até a posição de assentamento final. Após a polimerização, o material adere a armação metálica que foi removida da boca. Outra silicona por condensação média (3M) foi colocada sobre o material anterior, formando o corpo-de-prova, que foi seccionado longitudinalmente na região mais profunda do preparo. Sua espessura mostrou o grau de adaptação entre a fundição e o dente suporte. As medidas foram feitas utilizando projetor de perfil (MP320- Carl Zeiss, JENA). Os resultados foram analisados através do Teste de Mann-Whitney (5%), onde foi observada uma diferença significante (p=0,017) entre os dois grupos(Grupo A= 0,584 ± 0,325mm e Grupo B= 0,311 ± 0,237mm). Os apoios confeccionados sobre resina composta apresentaram uma melhor adaptação ao preparo para apoio do que os realizados sobre esmalte.

Consideraçöes clínicas sobre os princípios biomecânicos que orientam os preparos coronários em prótese parcial fixa / Clinical considerations about biomechanical principles which guide crown preparation in fixed partial denture

Conhecer os princípios mecânicos e biológicos que devem orientar a execuçäo dos preparos coronários em Prótese Parcial Fixa (PPF) é de extrema importância para a preservaçäo das estruturas de suporte e longevidade dos tratamentos reabilitadores. O clínico, ao estudá-los deveria ser capaz de determinar as áreas dos dentes a serem envolvidas, assim como a altura e tipo de acabamento das paredes dentárias, a melhor geometria dos preparos coronários, visando assegurar estabilidade e retençäo adequadas. É consenso que a estrutura dentária sadia deve ser preservada. Assim, o equilíbrio entre reduçäo "necessária" de tecido dentário sadio e o mínimo de agressäo ao tecido pulpar e periodontal deve ser alcançado. Quaisquer tipos de agressäo gerados pelos procedimentos operatórios devem ser minimizados: o desenvolvimento de calor pelos instrumentos rotatórios, a desidrataçäo e o contato da dentina desprotegida com substâncias agressivas devem ser evitados ou controlados. Ao planejarmos um preparo coronário, devemos saber qual a real necessidade de retençäo, pois essa necessidade varia conforme a extensäo do espaço edêntulo ou das exigências impostas pela oclusäo. A estabilidade é auxiliar direta da retençäo, pois mantém a integridade do relacionamento entre restauraçäo e dente preparado e principalmente, da adaptaçäo marginal. O bom senso, as evidências científicas e a correta aplicaçäo dos princípios preservadores e biologicamente protetores dos tecidos devem nortear os profissionais que se dedicam à prótese dentária

Restaurações estéticas - novas alternativas / Aesthetic restorations - new alternative

Novos materiais significam novas opções de tratamento bem como novos procedimentos operatórios, os quais possibilitam um Odontologia restauradora mais estética e na maior parte dos casos mais conservadora. Os autores apresentam um revisão da literatura dos materiais restauradores estéticos indiretos, mostrando algumas soluções clínicas para o seu uso na prática odontológica

Meios auxiliares de retenção para restaurações atípicas de amálgama - atualização clínica / Auxiliary means of retentions for atypical amalgam restorations - clinical atualization

Os autores apresentam uma atualização clínica sobre os meios auxiliares de retenções atípicas de amálgama: retenções naturais (canaletas, amalgapins - slots) e artificiais (pinos de retenção e amalgambond)